UP Resin

Product Details

Product Description

Unsaturated polyester resin

1: Hand lay-up General purpose

Code

Type

25℃  Pa.s

Viscosity

Min

gel time

%

Non-Volatile

Mpa

Tensile

strength

%

Elongation

Mpa

Flexural

Strength

HDT

Application

TK-806

PA

0.60-1.15

9.1-18.1

64-70

76

2.0

120

72

Flexibility,high impact strength

TK-189

PA

0.25-0.45

10-22

59-65

60

4.0

100

57

Water resistance, for boat.CCS

TK-191

PA

0.25-0.45

9-17

61-67

55

1.8

110

66

Translucent, general FRP purpose

TK-191RS

PA

0.25-0.45

9-17

61-67

60

3.5

114

70

For FRP product, general purpose

TK-195

PA

0.12-0.22

30-54

58-64

55

1.2

115

54

For Tramsparency FRP product

TK-196

PA

0.60-1.20

9.1-18.9

64-70

76

2.0

120

72

Flexibility, high strength, CCS

TK-198

PA

0.45-0.80

11-20

60-67

60

1.4

115

100

High thermal properties, high HDT, high strength

TK-580

IPA

0.40-0.70

10-20

66-70

15

68

10

67

Flexibilizer or flexible resin, with other resins

TK-1032

PA

0.25-0.65

15-23

15-23

60

2.0

105

67

Good mechanical property, for bus,boat, CCS approval

TK-22

PA

0.34-0.38

16-22

16-22

62

2.3

108

65

Pre-promoted, thixotropy and low shrinkage

TK-2068

PA

0.20-0.40

11-25

11-25

58

1.5

110

100

Hot water resistance and high HDT,for bathtub

TK-10070

PA

0.30-0.34

8-18

8-18

65

2.0

115

68

Low viscosity, rapid wetting reinforcement for high strength FRP products.

2:Flame retardant


Code

Type

25  Pa.s

Viscosity

Min

gel time

%

Non

-Volatile

Mpa

Tensile

strength

%

Elongation

Mpa

Flexural

Strength

Application

TK-107L

reactive

0.35-0.65

16-30

62-68

320


256

Flame retardant, for boat, ccs OI≥32

TK-107M

reactive

0.35-0.65

15-30

64-70

340


336

Flame retardant, for boat, OI≥34

TK-108

reactive

0.25-0.55

30-60

62-69

288


348

Flame retardant, transparency, OI≥32

TK-480

reactive

0.30-0.40

11-24

65-71

260


280

High flame retardant and low smoke emission, for railway FRP  OI≥36

TK-107XHA

reactive

0.30-0.45

11.5-23.5

65-71

250


260

High flame retardant and high strength, good processability,

Ccs approved, OI≥36

TK-802

filled

0.60-1.20

11-22


202


225

Flame retardant,filled type, general purpose FRP, OI≥30

TK-802P

filled

0.60-1.20

15-25


210


232

Pro-promoted, flame retardant, filled type, general purpose FRP OI≥30

TK-V1053

filled

0.40-0.80

10-20


261


232

No-halogen,high flame retardant, low smoke emission, for railway FRP, OI≥37

3:Chemical resistance

Code

Type

25  Pa.s

Viscosity

Min

gel time

%

Non

-Volatile

Mpa

Tensile

strength

%

Elongation

Mpa

Flexural

Strength

HDT

Application

TK-197

bisphenol

0.48-0.98

13-27

46-53

55

1.5

100

115

Good alkali resistance, for FRP etc

TK-199

IPA

0.40-0.80

12-22

58-64

55

1.5

95

120

High HDT or heat resistance, chemical resistance, for FRP pipe etc

4: Food grade

TK-196SP

PA

0.65-1.15

9.1-18.9

64-70

76

2.3

120

73

Food grade, lining resin, CNH approval

TK-198SP

PA

0.45-0.80

11-20

60-67

60

1.4

115

100

Food grade, CNH approval

5. Spray up

TK-1032

PA

0.14-0.54

15-30

58-64

60

2.0

120

65

Thixotropy, pre-promoted, for hand lay-up or spray up allocation to fabricate all kinds of FRP products, CCS approval

TK-1021

PA

0.38-0.54

12-22

58-64

58

1.6

110

66

Thixotropy, pre-promoted, for hand lay-up or spray up allocation to fabricate FRP products

6. For boat

TK-196

PA

0.60-1.20

9.1-18.9

64-70

76

2.0

120

72

General purpose, CCS approval

TK-107M

Reactive

0.58-0.65

15-30

64-70

50

1.5

85

70

Flame retardant, CCS approval

TK-1032TP

PA

0.45-0.55

10-20

58-64

60

2.0

100

65

Low shrinkage, thixotropy pre-promoted, CCS approval

TK-189

PA

0.25-0.45

10.5-21.5

59-65

60

4.0

100

57

Water and chemical resistance, high elongation, CCS approval

7. Button

Code

Type

25℃  Pa.s

Viscosity

Min

gel time

%

Non-Volatile

Mpa

Tensile

strength

%

Elongation

Mpa

Flexural

Strength

HDT

Application

TK-253

IPA

0.90-1.05

5-10

64-70

60

3.0

100

70

High impact strength

TK-2001

PA

0.75-1.05

8-12

64-70

48

1.5

98

53

Good gloss and transparency

TK-20750

IPA

0.90-1.05

15-20

64-70

58

3.4

90

55

High impact strength

8.For pultrusion and RTM

TK-107P

Reactive

0.30-0.50

6-12

65-71

50

3.0

120

80

High HDT, flame retardant, for FRP products, CCS approval

TK-1003

PA

0.35-0.55

7-10

59-65

48

1.2

170

90

Rigid, for producing fishing pole, tent pole, grille, etc

TK-2093

IPA

0.35-0.45

7-9

54-60

80

3.8

130

112

Heat and chemical resistance, for FRP products

TK-10200

PA

0.35-0.55

3-5.5

59-65

69

2.55

130

76

General purpose, for FRP pultrusion products

TK-1

PA

0.20-0.28

20-30

57-63

63

3.0

118

67

Low viscosity, pre-promoted, rapid wetting, for injection molding

TK-6007

PA

0.20-0.48

8-16

57-64

65

3.4

105

50

Low viscosity & shrinkage, easy operation for RTM

TK-21

PA

0.14-0.18

50-80

54-60

55

1.8

128

78

Pre-promoted, low PET, used in vacuum assisted resin injection molding

9. For FW pipe

Code

Type

25℃  Pa.s

Viscosity

Min

gel time

%

Non-Volatile

Mpa

Tensile

strength

%

Elongation

Mpa

Flexural

Strength

HDT

Application

TK-102

IPA

0.20-0.40

7-13

51-57

64

2.0

115

105

For lining, good flexibility, chemical resistance and high HDT, for water supply and drainage pipe, petroleum pipe and chemical industry pipe, tank

TK-191FW

PA

0.30-0.50

15-30

60-67

65

2.5

120

81

For structure, flexible and good mechanical property for FW pipe and tanks

TK-1900

PA

0.30-0.40

30-35

62-68

65

2.5

120

70

For structure, low PET and crack resistance

TK-196SPFW

PA

0.30-0.50

8.5-17.5

60-68

70

2.0

120

70

For lining, to make FW pipe and tanks, food grade, CNH approval

TK-20820

IPA

0.22-0.48

9-21

58-64

72

3.2

120

86

For lining, to make FW pipe and tanks, food grade, CNH approval

TK-10600

PA

0.20-0.26

5-12

55-61

68

2.7

138

81

For structure and HOBAS pipe

TK-503831

PA

0.20-0.40

5.5-12.5

56-62

11

76



High elongation for lining and HOBAS pipe, food grade, CNH approval

10. For paint

TK-196YK

PA

0.70-1.10

10-18

64-70

76

2.0

120

72

Good surface smoothness, excellent chemical resistance, for piano, furniture etc, hand lay up

TK-196GZ

PA

0.30-0.50

10-18

59-65

74

1.8

125

75

Good surface smoothness, good workability, for curtain

TK-8001P

PA

S-U

7-13

54-60

62

2.5

120

75

Thixotropy, high hardness, for curtain

TK-8001S

PA

0.30-0.50

8-14

54-60

65

2.7

120

75

Thixotropy, high hardness, for spray up

11. For translucent panel

Code

Type

25℃  Pa.s

Viscosity

Min

gel time

%

Non-Volatile

Mpa

Tensile

strength

%

Elongation

Mpa

Flexural

Strength

HDT

Application

TK-108

Reactive

0.25-0.55

30-60

62-69

62

2.8

123

56

Low viscosity and flame retardant

TK-10170

PA

0.13-0.25

7.5-14.5

54-60

56

1.8

115

73

Good light transmission and weather resistance, for hand lay up

TK-195

PA

0.12-0.24

28-56

58-64

55

1.2

115

54

Good light transmission and weather resistance, to make panels

12. Cultured marble

TK-1014

PA

0.30-0.40

4-8


65

3.0

120

56

Good transparency to casting crystal handcraft

TK-2006

IPA

0.30-0.45

5-9


76

4.2

120

72

Heat resistance, high elongation & impact strength, good workability for tabletop in kitchen

TK-10940

PA

1.25-1.80

4-11

67-71

55

6.2

103

60

Water & crack resistance, high elongation, for bath tub

TK-10950

PA

0.80-1.20

7-15

63-70

70

3.5

110

68

Good transparency and mechanical property

TK-1065

PA

0.60-0.80

12-25

66-71

68

1.8

106

90

Fast curing, good heat resistance and transparency for sanitary in bath room

TK-10140

PA

1.30-1.70

8-16


65

3

120

56

Excellent transparency to cast crystal handcraft

13. SMC/BMC

Code

Type

25℃  Pa.s

Viscosity

Min

gel time

%

Non-Volatile

Mpa

Tensile

strength

%

Elongation

Mpa

Flexural

Strength

HDT

Application

TK-109

PA

1.5-2.0

9-18

67-73

65


93

91

General purpose, heat resistance, for production of SMC/BMC

TK-198

PA

0.45-0.80

11-20

60-67

60

1.4

115

100

General purpose, heat resistance, for production of SMC

TK-1008

PA

X-Z

3.5-6.5


57

2.13

96

135

High strength, low shrinkage, good surface, heat resistance, for production of SMC/BMC

TK-2006S

IPA

2.5-3.5

10-12

64-67

60

2.2

100

120

High strength, heat resistance, for production of electrical parts and sanitary ware

TK-5002

NPG

0.60-0.80

6-8

60-66

50

1.8

80

110

Glossy surface, heat resistance, for sanitary ware

TK-40094

PA

0.90-1.20

12-24

57-63

58

1.8

82

120

Weather resistance, heat & water resistance, for water tank, sanitary ware and auto parts

 

CHANGZHOU UTEK COMPOSITE COMPANY CO.,LTD
COMPANY INTRODUCTION:
Company NameCHANGZHOU UTEK COMPOSITE CO.,LTD
AddressFuhanyuan 1-814Taihu RoadChangzhouJiangsuChina
Contact PersonNameTelEmail ID
MangerGong Xiaojun0086 13357899376gong@utekcomposite.com
MangerIrene Xi0086 13961156380irene@utekcomposite.com
Business ConditionManufactureTrading
Consititution of companyPvt.Ltd
Annual turnoverUSD10,000,000
Company Occupy Areas(M2)3000M2
Shower room Occupy Areas(M2)200M2
websitewww.utekcomposite.com
http://utekcomposites.en.made-in-china.com/
Mainly Customer & MarketingEurope,Asia,America,Middle East
Mainly ProductFiberglass chopped strand mat (powder and emulsion), stitch mat, combo mat, uni-direction and biaxial fabric, RTM core mat, woven roving, special products like Ar-glass roving, chopped strand, thin fiberglass fabric, SMC(sheet molding compound), fiberglass/polyester geogrid and geocomposite. fiberglass mica fabric for insulation.
Sales Team15University GraduatesProduct Team150
Research & Development Team12QC Team8
CertificateISO 9001 ,ISO 14001 ,SGS
Give us a chance, and we' ll return you with satisfaction. 

Feedback